Manufacturing process for obtaining integrated structure bipolar transistors with controlled storage time

ABSTRACT

Integrated structure bipolar transistors with controlled storage time are manufactured by forming at least one bipolar transistor occupying a first area on a first surface of the silicon material, covering the first surface of the silicon material with an insulating material layer, and selectively removing the insulating material layer to open a window. The window has a second area much smaller than the first area occupied by the bipolar transistor. Therefore, by implanting into the silicon material a medium dose of platinum ions through the window and diffusing into the silicon material the implanted platinum ions, a uniform distribution of platinum inside the transistor is obtained.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to integrated structure bipolar transistors with a controlled storage time, and a manufacturing process for obtaining such devices.

2. Discussion of the Related Art

In bipolar transistors, the "storage time" is a parameter defining the time necessary for the device to move from the saturation region to the active region, and depends on the biasing conditions and on the minority carrier lifetime in the base and collector regions of the transistor.

In several applications, such as lamp ballast circuits, it is advantageous to use power a bipolar transistors with a highly controlled storage time, in order to avoid adverse affects on the circuit oscillation frequency and the power delivered to the load. In view of such applications, the manufacturers make available different selections of transistors with guaranteed storage time values, with tolerances normally limited to 20% of the specified value.

One way to assure such a fine tuning of the storage time is to prevent the bipolar transistor from being driven into deep saturation, by means of circuital techniques such as those described in the European Patent Application No. 93830261.9.

Another way is to make use of techniques for controlling the minority carrier lifetime. In the practice, this means reducing the minority carrier lifetime from about 30 μs to 10-20 μs, depending on the specific application.

One known lifetime-control technique calls for exposing the device to electron radiation. In this technique, silicon atoms in the lattice are displaced from their sites, and deep energy levels are introduced in the silicon energy band gap. Such deep energy levels cause a variation of the minority carrier lifetime, which can therefore be controlled.

However, this technique has some limitations. First, electron-hole pairs are created at the interface between the silicon surface and the silicon dioxide layer, reducing the device reliability. Second, the damage produced in the lattice by the displacement of silicon atoms from their sites is unstable and varies with temperature and time. In fact, submitting the device to temperatures in the range of 280°-400° C. will re-establish in the lattice the conditions that existed before the exposure to the electron radiation, thereby destroying the controlled storage time. This is because during its packaging the device is submitted to a thermal process ("die attach") at temperatures ranging from approximately 300° C. to 350° C., and therefore the precision of the minority carrier lifetime tuning is compromised.

Another known lifetime-control technique calls for the introduction of platinum atoms. In this technique, the tuning of the minority carrier lifetime thus achieved is not affected even if the device is successively submitted to temperatures ranging from approximately 400° C. to 600° C.

The minority carrier lifetime T is normally related to the dose of platinum atoms introduced into the silicon by the following equation:

    (l/τ)-(l/τ0)=K.sub.pt ×D

where τ0 is the minority carrier lifetime before the introduction of platinum atoms, K_(Pt) is a constant for platinum, and D is the dose of platinum atoms introduced. It is therefore necessary to introduce extremely low doses of platinum atoms, ranging from 10¹⁰ to 10¹¹ atoms/cm², since for doses of the order of 10¹² atoms/cm² the minority carrier lifetime falls to values of some microseconds, which are too low for the applications under consideration. Such low doses cannot be statistically reproduced by any known implanting industrial apparatus. In fact, the dispersion between different implants could be higher than 50%, and would make the technique disadvantageous to be industrialized. The introduction of platinum atoms by means of the deposition technique is even more inadequate to achieve such low doses.

SUMMARY OF THE INVENTION

In view of the state of the art described, an object of the present invention is to provide a manufacturing process for obtaining bipolar transistors with controlled storage time by means of the introduction of platinum atoms into silicon, in a manner which overcomes the above-mentioned difficulties.

According to the present invention, this and other objects are attained by means of a manufacturing process for obtaining integrated structure bipolar transistors with controlled storage time including the steps of:

a) in a silicon material, forming at least one bipolar transistor occupying a first are on a first surface of the silicon material;

b) covering the first surface of the silicon material with an insulating material layer;

c) selectively removing the insulating material layer to open at least one window having a second area much smaller than the first area occupied by the bipolar transistor;

d) implanting into the silicon material a medium dose of platinum ions through said window;

e) diffusing into the silicon material the implanted platinum ions to obtain a uniform distribution of platinum inside the transistor.

As a result of embodiments of the present invention, it is possible to implant platinum ions with implant doses which are easy to control by using existing implanting apparatus. After thermal diffusion, the platinum ions are uniformly distributed in the device, and since the area of implantation is much smaller than the area of the device, the concentration of platinum is equivalent to that which will be obtained if the whole device surface would be implanted with a much lower dose of platinum ions, at a level which was impractical prior to this invention. The storage time of the device can thus be finely tuned.

BRIEF DESCRIPTION OF THE DRAWINGS

The features of the present invention will be made more evident by the following detailed description of several practical embodiments, illustrated as non-limiting examples in the annexed drawings:

FIG. 1 is a top plan view of a portion of a semiconductor wafer, taken at an intermediate step of a manufacturing process according to an embodiment of the present invention.

FIG. 2 is a cross-sectional view of the portion of wafer taken along the line II--II of FIG. 1.

FIG. 3 is a top plan view of said portion of wafer, taken at another intermediate step of the manufacturing process.

FIG. 4 is a cross-sectional view of the portion of wafer taken along the line IV--IV of FIG. 3.

FIG. 5 is a cross-sectional view similar to FIG. 4, taken at a third intermediate step of the manufacturing process.

FIG. 6 is a top plan view similar to that of FIG. 3, taken at an intermediate step of a manufacturing process according to another embodiment of the present invention.

DETAILED DESCRIPTION

A manufacturing process according to an embodiment of the invention starts with a silicon wafer heavily doped to form an N+ substrate 1, as skown in FIG. 2.

Over the substrate 1 a lightly doped N- layer 2 is grown, for example epitaxially, with resistivity and thickness determined on the basis of the breakdown voltage desired for the bipolar transistors which are to be fabricated. The N- layer 2, also shown in FIG. 2, constitutes a collector region of the bipolar transistors.

Acceptor-type dopant impurities are then selectively introduced, according to any known technique, into the N- layer 2 (for example by means of ion implantation and diffusion), to form heavily doped P+ regions 3, substantially with square shape, each constituting a base region of a respective bipolar transistor. As shown in FIG. 1, the P+ regions 3 are normally disposed to form a bidimensional array on the wafer surface.

Donor-type dopant impurities are then selectively introduced into the P+ regions 3 to form N+ regions 4, each one constituting an emitter region of said respective bipolar transistor. As shown in FIG. 1, the N+ regions 4 can for example have a comb-like shape, to increase emitter efficiency.

The wafer is then oxidized, and an oxide layer 5 thus formed is selectively removed from the surface of the wafer to open windows 6 to expose selected areas of the wafer surface. As shown in FIG. 3, the windows 6 may be located along the sides of the P+ regions 3. In one arrangement, each P+ region 3 is surrounded by four windows 6.

Platinum ions are then selectively implanted into the wafer surface with an implantation dose D (atoms/cm²), with the oxide layer 5 acting as a mask. Platinum ions can therefore be introduced into the N- layer 2 only in correspondence of the windows 6. The platinum ions thus introduced are then made to diffuse, for example, by heating the wafer to a temperature ranging from 850° C. to 1000° C. At the end of this step the platinum ions are uniformly distributed in the bulk of the silicon wafer.

Each window 6 has an area A_(Pt) /2. Since the platinum ions introduced through each window 6 diffuse isotropically into the silicon, they are shared by two adjacent devices. Each window 6 contributes therefore for an area A_(Pt) /4 to the area of implantation of platinum ions per device. Since each device is surrounded by four windows 6, the area of implantation of platinum ions per device is globally A_(Pt). Assuming that the area occupied on the wafer surface by each device is A_(D), substantially corresponding to the area of the P+ base region 3, after the diffusion the concentration of platinum in each device corresponds to that which will be obtained if an equivalent dose Deq of platinum ions would be implanted into the whole area A_(D) of the device, with Deq being given by:

    Deq=D×A.sub.Pt /A.sub.D

By making the window areas A_(Pt) /2 very small, so that A_(Pt) is much lower than A_(D), it is possible to obtain a value for the equivalent dose Deq of implanted platinum ions which is very low, even if the effective implant dose D is kept in a range of values sufficiently high to allow the use of the existing implanting apparatus, and to be reproducible. If for example the device area is A_(D) =10 mm and A_(Pt) =0.01 mm², the factor A_(Pt) /A_(D) is 1/1000 and for an implantation dose D=10¹³ at/cm² there is obtained an equivalent implantation dose Deq=10¹⁰ at/cm². Decreasing the window area, or keeping the same window area for larger devices, lower equivalent implantation doses of platinum can be obtained. In this way it is possible to introduce into the silicon wafer a controlled amount of platinum ions which is reproducible, and which therefore yields bipolar transistors with a controlled storage time, with a minority carrier lifetime in an exemplary desired range of 10 to 20 μs.

The diffusion step of the implanted platinum ions is carried out after all the other thermal steps in the manufacturing process have been performed. It has been experimentally verified that with a temperature of approximately 850°-1000° C., a few hours are sufficient to obtain a uniform distribution of the platinum ions over the whole wafer. Since the diffusion steps utilized for the manufacturing of power devices call for high temperature processes of approximately 1100°-1200° C. and long times (approximately 5-15 hours), the diffusion process of the platinum ions do not alter the junction depths of the layers.

After the introduction of platinum, the oxide layer 5 may be selectively removed to form contact holes, and a metal layer 7 may be deposited over the wafer surface and selectively etched to provide electrical contacts to the P+ base regions 3 and to the N+ emitter regions 4 of the various devices, as show in FIG. 50 The oxide layer 5 may also be removed along the sides of the devices to facilitate the device cutting by means of mechanical or laser scribing.

According to a second embodiment of the present invention, shown in FIG. 6, if the device area A_(D) is of the order of 1 cm², the windows 6 in the oxide layer 5 can be opened over the devices, instead that along their sides. This makes it possible to obtain, after implantation and diffusion, a uniform distribution of platinum ions in the silicon wafer, without increasing the temperature and/or the time duration of the platinum diffusion steps. The distribution of windows 6 over each device can be varied, the only requirement being that the overall area A_(Pt) of the device exposed to the implantation of platinum ions is much smaller than the device area A_(D). In the shown example, four windows 6 per device have been opened, each window 6 having an area A_(Pt) /4.

Even if the process according to the invention has been described with reference to the fabrication of controlled storage time NPN bipolar transistors, it is evident to anyone skilled in the art that it can as well be used for the fabrication of controlled storage time PNP transistors, by exchanging the P-type semiconductor regions with N-type, and exchanging the N-type regions with P-type.

Having thus described at least one illustrative embodiment of the invention, various alterations, modifications, and improvements will readily occur to those skilled in the art. Such alterations, modifications, and improvements are intended to be within the spirit and scope of the invention. Accordingly, the foregoing description is by way of example only and is not intended as limiting. The invention is limited only as defined in the following claims and the equivalents thereto. 

What is claimed is:
 1. A process for manufacturing bipolar transistors with a controlled storage time comprising the steps of:a) forming a bipolar transistor occupying a first area on a first surface of a silicon material; b) covering the first surface of the silicon material with an insulating material layer; c) selectively removing the insulating material layer to open a window having a second area that is smaller than the first area, the window being adjacent but not directly over the first area occupied by the bipolar transistor; d) implanting into the silicon material a dose of platinum ions through said window; and e) diffusing into the silicon material the implanted platinum ions, so that the implanted platinum ions diffuse into the silicon material in the first area occupied by the bipolar transistor.
 2. The process of claim 1, further including a step of determining said dose of platinum from a ratio between the first area and the second area.
 3. The process of claim 2, wherein said dose of platinum ions and said ratio are determined so that after the step e), a uniform distribution of platinum ions with a concentration in a range of 10¹² atoms/cm³ to 10¹³ atoms/cm³ is obtained.
 4. The process of claim 1, wherein step a) includes forming a plurality of uniformly distributed bipolar transistors, each having a transistor area, and step c) includes selectively removing the insulating material layer to open a plurality of uniformly distributed windows, each having a window area, wherein a total area of the plurality of uniformly distributed windows is substantially smaller than a total area of the plurality of bipolar transistors.
 5. The process of claim 4, wherein each window of the plurality of uniformly distributed windows is located between two respective adjacent bipolar transistors of the plurality of uniformly distributed bipolar transistors.
 6. The process of claim 5, wherein the plurality of uniformly distributed windows are uniformly distributed about the plurality of uniformly distributed bipolar transistors.
 7. The process of claim 1, wherein a ratio of the first area to the second area is approximately 1000:1.
 8. A process for manufacturing a bipolar transistor with a controlled storage time, comprising the steps of:a) forming at least one bipolar transistor occupying a first area on a first surface of a silicon material; b) covering the first surface of the silicon material with an insulating material layer; c) selectively removing the insulating material layer to open at least one window having a second area that is substantially smaller than the first area; d) implanting into the silicon material a first dose of platinum ions through said at least one window; and e) diffusing into the silicon material the implanted platinum ions to obtain a uniform distribution of platinum inside the bipolar transistor with a concentration that is equal to a concentration obtained by implanting into an area substantially equal to said first area a second dose of platinum ions substantially lower than said first dose, said concentration controlling the storage time of the bipolar transistor; wherein: said prescribed concentration of platinum inside the bipolar transistor ranges from approximately 10¹² atoms/cm³ to approximately 10³ atoms/cm³ ; and a ratio between the second area and the first area is approximately 1/1000, and said first dose of platinum ions is approximately 10¹³ atoms/cm².
 9. The process of claim 8, wherein said first dose of platinum ions is determined from said prescribed concentration, and a ratio between the first area of the bipolar transistor and the second area.
 10. The process of claim 8, wherein in step c), a plurality of uniformly distributed windows are opened, a total area of said plurality of windows being substantially smaller than the first area of the bipolar transistor.
 11. The process of claim 10, wherein the windows of said plurality of uniformly distributed windows are located adjacent to the bipolar transistor.
 12. The process of claim 10, wherein the windows of said plurality of uniformly distributed windows are located directly over the bipolar transistor.
 13. The process of claim 8, wherein in step a) a plurality of uniformly distributed bipolar transistors is formed, each having a first area, and in step c) a plurality of uniformly distributed windows is formed, each having a second area, a sum of the second areas of all of the plurality of windows being substantially smaller than a sum of the first areas of all of the plurality of bipolar transistors.
 14. The process of claim 13, wherein each window of said plurality of uniformly distributed windows is located between two respective adjacent bipolar transistors of the plurality of uniformly distributed bipolar transistors.
 15. The process of claim 13, wherein the windows of the plurality of uniformly distributed windows are uniformly distributed about the bipolar transistors of the plurality of uniformly distributed bipolar transistors.
 16. The process claim 13, wherein each window of the plurality of uniformly distributed windows is located directly over a corresponding bipolar transistor of the plurality of uniformly distributed bipolar transistors.
 17. A method for implanting ions into a bipolar transistor which has been formed on a substrate, the substrate having a surface area, the method comprising the steps of:implanting only a part of a dose of ions into only a portion of the substrate that has a surface area which is less than a surface area of the bipolar transistor, the portion of the substrate being based upon a concentration of the dose of ions and a predetermined resulting concentration of ions in the bipolar transistor, the predetermined resulting concentration of ions being sufficient to control a storage time of the bipolar transistor; and diffusing the part of the dose of ions from the portion of the substrate through substantially an entire area of the bipolar transistor; wherein:the ions are platinum ions; the step of implanting includes the steps of: a) covering an entire surface of the substrate with a mask: b) etching away a portion of the mask over said portion of the substrate to expose the penetration portion; and c) exposing the surface area of the substrate to the dose of ions, so that ions are only implanted through said etched portion of said mask; the bipolar transistor has a first area, and the penetration portion of the substrate has a second area substantially Smaller than the first area; and a ratio of the first area to the second area is approximately 1000:1.
 18. The method of claim 17, wherein the step of diffusing includes diffusing the part of the dose of platinum ions so that a uniform concentration of platinum ions is distributed in the substrate at a concentration of approximately in a range of 10¹² atoms/cm³ to 10¹³ atoms/cm³.
 19. The method of claim 17, wherein the portion of the substrate includes a plurality of uniformly distributed sections.
 20. The method of claim 19 wherein each of the plurality of uniformly distributed sections is located adjacent to the bipolar transistor.
 21. The method of claim 19 wherein each of the plurality of uniformly distributed sections is located in the bipolar transistor.
 22. A process for manufacturing a bipolar transistor with a controlled storage time, comprising the steps of:a) forming at least one bipolar transistor occupying a first area on a first surface of a silicon material; b) covering the first surface of the silicon material with an insulating material layer; c) selectively removing the insulating material layer to open at least one window having a second area that is substantially smaller than the first area; d) implanting into the silicon material a first dose of platinum ions through said at least one window; and e) diffusing into the silicon material the implanted platinum ions to obtain a uniform distribution of platinum inside the bipolar transistor with a concentration that is equal to a concentration obtained by implanting into an area substantially equal to said first area a second dose of platinum ions substantially lower than said first dose, said concentration controlling the storage time of the bipolar transistor;wherein: in step c), a plurality of uniformly distributed windows are opened, a total area of said plurality of windows being substantially smaller than the first area of the bipolar transistor; and the windows of said plurality of uniformly distributed windows are located adjacent to the bipolar transistor.
 23. A process for manufacturing a bipolar transistor with a controlled storage time, comprising the steps of:a) forming at least one bipolar transistor occupying a first area on a first surface of a silicon material; b) covering the first surface of the silicon material with an insulating material layer; c) selectively removing the insulating material layer to open at least one window having a second area that is substantially smaller than the first area; d) implanting into the silicon material a first dose of platinum ions through said at least one window; and e) diffusing into the silicon material the implanted platinum ions to obtain a uniform distribution of platinum inside the bipolar transistor with a concentration that is equal to a concentration obtained by implanting into an area substantially equal to said first area a second dose of platinum ions substantially lower than said first dose, said concentration controlling the storage time of the bipolar transistor;wherein: in step a) a plurality of uniformly distributed bipolar transistors is formed, each having a first area; in step c) a plurality of uniformly distributed windows is formed, each having a second area, a sum of the second areas of all of the plurality of windows being substantially smaller than a sum of the first areas of all of the plurality of bipolar transistors; and each window of said plurality of uniformly distributed windows is located between two respective adjacent bipolar transistors of the plurality of uniformly distributed bipolar transistors.
 24. A method for implanting ions into a bipolar transistor which has been formed on a substrate, the substrate having a surface area, the method comprising the steps of:implanting only a part of a dose of ions into only a portion of the substrate that has a surface area which is less than a surface area of the bipolar transistor, the portion of the substrate being based upon a concentration of the dose of ions and a predetermined resulting concentration of ions in the bipolar transistor, the predetermined resulting concentration of ions being sufficient to control a storage time of the bipolar transistor; and diffusing the part of the dose of ions from the portion of the substrate through substantially an entire area of the bipolar transistor;wherein: the penetration portion of the substrate includes a plurality of uniformly distributed sections; and each of the plurality of uniformly distributed sections is located adjacent to the bipolar transistor. 